Material: Titanium Alloy
Composition: Titanium 6Al-6V-2Sn
UNS Code: UNS R56620
Standard: AMS4971
Forms typically available: Bars, Wire, Forgings, and Rings
Free sample: Availabele
Certificate: EN10204-3.1, ISO9001,aerospace certificate

Send Inquiry

Description

Products Description

+86 17719616665

6AL-6V-2SN (Ti 6-6-2) is a highly beta stabilized, two-phase alloyed Grade of alpha-beta Titanium. Ti 6-6-2 is similar to 6AL-4V in many ways but exhibits higher strength properties due to the addition of Vanadium, Iron, and Copper. It is often found in the Annealed condition or heat-treated to the higher strength Solution Treated & Aged condition.

Ti-662 6Al-6V-2Sn Composition

Element	Min	Max
Aluminum	5	6
Vanadium	5	6
Tin	1.5	2.5
Iron	0.35	1
Copper	0.35	1
Carbon	--	0.05
Oxygen	--	0.2
Nitrogen	--	0.04 (400 ppm)
Hydrogen	--	0.015 (150 ppm)
Yttrium	--	0.005 (50 ppm)
Other Elements, each	--	0.1
Other Elements, total	--	0.4
Titanium	remainder

Ti-662 6Al-6V-2Sn Minimum tensile properties, inch/pound units

Nominal Diameter or Least Distance Between Parallel Sides	Tensile Strength	Yield Strength at 0.2% Offset	Elongation in 4D	Elongation in 4D	Reduction of Area	Reduction of Area
Inches	ksi	ksi	%	%	%	%
			L	T	L	T
Up to 1.000, incl	175	160	8	6	20	15
Over 1.000 to 2.000, incl	170	155	8	6	20	15
Over 2.000 to 3.000, incl	155	145	8	6	20	15
Over 3.000 to 4.000, incl	150	140	8	6	20	15

Ti-662 6Al-6V-2Sn Minimum tensile properties, SI units

Nominal Diameter or Least Distance Between Parallel Sides	Tensile Strength	Yield Strength at 0.2% Offset	Elongation in 4D	Elongation in 4D	Reduction of Area	Reduction of Area
Millimeters	MPa	MPa	%	%	%	%
			L	T	L	T
Up to 25.40, incl	1207	1103	8	6	20	15
Over 25.40 to 50.80, incl	1172	1069	8	6	20	15
Over 50.80 to 76.20, incl	1069	1000	8	6	20	15
Over 76.20 to 101.60, incl	1034	965	8	6	20	15